NOTICE RE: GEL PATINAS
RESTORING GEL VISCOSITY During extended periods of storage or in cold weather, the gels can become too stiff to use effectively. Temps <32°F will cause the gels to become very stiff. If I add approved ...
Read more→
DON’T USE SOLVENTS
QUESTION: I am having some trouble with one of my favorite patinas not “sticking” in certain spots. Any suggestions? Brian B. ANSWER: (Note: This is one of the most common questions I receive. Problems with ...
Read more→
COLOR CASE-HARDENING FAQ'S LATEST NEWS! QUESTIONS & ANSWERS SPECIALTY FINISHES TIPS & TRICKS UNIQUE FINISHES
New Video – Color Case Hardening Gel Patinas
DO IT YOURSELF! COLOR CASE-HARDENING PATINAS & PROCEDURES FOR GUNS, GUN PARTS & KNIFE BLADES. [embedyt] https://www.youtube.com/watch?v=441iuqp1Vq0&width=740&height=416[/embedyt]
Read more→
FAQ'S LATEST NEWS! NEW PRODUCTS QUESTIONS & ANSWERS SPECIALTY FINISHES TIPS & TRICKS UNIQUE FINISHES
Steel Patina “PRO STARTER KIT” – Save Up to 15%
“PRO STARTER KIT” STEEL PATINAS “PRO STARTER KIT” ~ Each Ultra-Premium Steel Patina Product is Discounted 10%-15% and You Build Your Own Kit, Including Size & Quantities of Each. (Limit 2 Per Product). Includes Trigger-Spray Bottles ...
Read more→
STEEL F/X® PATINAS – WORK YEAR ROUND!
Winters or Freezing Weather Won’t Stop You From Doing Patina or Dye Work on Steel Art, or Other Metals, As There Are Several Ways to Get The Necessary Water To Your Work-Piece or Work Area. Below ...
Read more→
FAQ PAGE
Would you like to learn some things about the patination of steel that you may not already know? Please check out this FAQ Page Thanks, Bill
Read more→
COLOR-FINISHING THE “U.S. TATTERED FLAG”
COLOR-FINISHING THE “U.S. TATTERED FLAG” 3 METHODS. The U.S. Tattered Flag, has been and remains one of the most popular plasma-cut, color-finished pieces. Here are just 3 methods that different artisans are using. If ...
Read more→
COLOR CASE HARDENING COLOR CASE-HARDENING FAQ'S LATEST NEWS! QUESTIONS & ANSWERS SPECIALTY FINISHES TIPS & TRICKS UNIQUE FINISHES
Color Case-Hardening Effect on Steel
STEEL F/X® Patinas Specially Developed for Creating a Color Case-Hardened Finish. Hi Bill, I have a modern S&W shotgun that is color case-hardened. Being my first exposure to the art of CCH, I did ...
Read more→
TORCH F/X™ – RED/BLUE PATINA FOR STEEL
TORCH F/X™ – RED/BLUE PATINA FOR STEEL ART. New, Updated Video! Please take a look when you have time. Thanks, Bill [embedyt] https://www.youtube.com/watch?v=YOEsXkHwmkA[/embedyt]
Read more→
FAQ'S LATEST NEWS! QUESTIONS & ANSWERS STEEL PREPARATION TIPS & TRICKS Uncategorized UNIQUE FINISHES
Oil Removal from Steel?
QUESTION: Hi Bill! Would you kindly let me know how to clean cold rolled steel in preparation for your products? I’m not worried about slag, dross, etc. I will use flap discs for sanding/polishing ...
Read more→
FAQ'S LATEST NEWS! NEW PRODUCTS QUESTIONS & ANSWERS SPECIALTY FINISHES TIPS & TRICKS UNIQUE FINISHES
Introducing: SNART™ COLOR PROCESS FOR METAL
STEEL F/X® PATINAS is Proud to Announce The Development of a Brand New Coloring Medium: SNART™ SNART™ is an Easy, Exciting New Process for Colorizing Your Art (METAL COLORING MEDIUM), or Any Other Project that ...
Read more→