Amazing Patina Work!
Read more→
NOTICE RE: GEL PATINAS
RESTORING GEL VISCOSITY During extended periods of storage or in cold weather, the gels can become too stiff to use effectively. Temps <32°F will cause the gels to become very stiff. If I add approved ...
Read more→
FAQ PAGE
Would you like to learn some things about the patination of steel that you may not already know? Please check out this FAQ Page Thanks, Bill
Read more→
COLOR-FINISHING THE “U.S. TATTERED FLAG”
COLOR-FINISHING THE “U.S. TATTERED FLAG” 3 METHODS. The U.S. Tattered Flag, has been and remains one of the most popular plasma-cut, color-finished pieces. Here are just 3 methods that different artisans are using. If ...
Read more→
COLOR CASE HARDENING COLOR CASE-HARDENING FAQ'S QUESTIONS & ANSWERS SPECIALTY FINISHES TIPS & TRICKS UNIQUE FINISHES
Color Case-Hardening Effect on Steel
STEEL F/X® Patinas Specially Developed for Creating a Color Case-Hardened Finish. Hi Bill, I have a modern S&W shotgun that is color case-hardened. Being my first exposure to the art of CCH, I did ...
Read more→
TORCH F/X™ – RED/BLUE PATINA FOR STEEL
TORCH F/X™ – RED/BLUE PATINA FOR STEEL ART. New, Updated Video! Please take a look when you have time. Thanks, Bill
Read more→
DON’T USE SOLVENTS
QUESTION: I am having some trouble with one of my favorite patinas not “sticking” in certain spots. Any suggestions? Brian B. ANSWER: (Note: This is one of the most common questions I receive. Problems with ...
Read more→
Oil Removal from Steel?
QUESTION: Hi Bill! Would you kindly let me know how to clean cold rolled steel in preparation for your products? I’m not worried about slag, dross, etc. I will use flap discs for sanding/polishing ...
Read more→
Introducing: SNART™ COLOR PROCESS FOR METAL
STEEL F/X® PATINAS is Proud to Announce The Development of a Brand New Coloring Medium: SNART™ SNART™ is an Easy, Exciting New Process for Colorizing Your Art (METAL COLORING MEDIUM), or Any Other Project that ...
Read more→